Aluminium Filler Wire

Er4043 Aluminum Filler Wire

Product Details:
  • Wire Material: Aluminium/Aluminium Alloy
  • Thickness: 2 mm, 4 mm
  • Quantity Per Roll: 10 kg, 20 kg
  • Weight: 6-7kg

Er4043 Aluminum Filler Wire

ER4043 Aluminum filler materials are silicon types for welding of 2014, 5052, 6061, 6101 and 6063. Use with DC Reversed Polarity (DCEP). shielding gas, ARGON, is required.

Typical uses include: Truck bodies, pressure vessels, structural members, petroleum distribution equipment.

Er4047 Aluminum Filler Wires

Product Details:
  • Wire Material: Aluminium/Aluminium Alloy
  • Thickness: 3 mm
  • Quantity Per Roll: 20 kg

Er4047 Aluminum Filler Wires Aluminum wires and rods for welding and brazing. Good mechanical characteristics, their excellent corrosion resistance and low melting point ensure a very low number of deformations in the origin metal. This material is generally used for brazing aluminum sheets, for extrusions and castings. (After anodizing the welding will be of a different colour)

Chemical composition:
 
Si11.0-13.0 , Fe <0.50, Cu <0.05, Mn <0.15, Mg <0.05,
Zn<0.10, Ti < 0.15, Al remainder

Minimal Values of the Mechanical Properties (Welded Metal):
 
Tensile strengthRm : 130 N/mm2
Yield StrengthRp 0, 2 : 60 N/mm2
ElongationL=5d:5%
Melting range573-585 deg. C

Er5356 Aluminum Filler Wires

Product Details:
  • Wire Material: Aluminium/Aluminium Alloy
  • Thickness: 4 mm
  • Quantity Per Roll: 15 kg
  • Packaging (kg per pack): 100-200

Er5356 Alumunium Filler Wires

Application:

  • ER5356 materials are used mainly for welding aluminum of like composition. This type is also useful if color match is important after anodizing.
  • The proper choice of aluminum filler metal mainly depends on the base metal properties to be achieved andwelding technique. Post weld cracking, corrosion resistance and behavior under elevated temperature also needto be taken into consideration.
  • Cracking usually can be minimized by choosing a filler metal alloy of higher alloy content then the base metal.

 

Composition:

  • Deposited Chemical Composition % (Typical)
  • Deposited chemistry is influenced by many factors so no typical analysis can be reported.
  • Deposited All Weld Metal Properties %
  • As-Welded
  • Deposited all weld metal properties are influenced by many factors such as weld process used, so no typical weld metal properties can be reported.

Er5183 Aluminum Filler Wire

Product Details:
  • Wire Material: Aluminium/Aluminium Alloy
  • Thickness: 4 mm
  • Quantity Per Roll: 15 kg
  • Grade: Brass

Er5183 Aluminum Filler Wire

Application:

  • ER5183 can be used on type base materials 5083 and 5456. Not recommended for sustained elevated temperature service. Assure proper storage to avoid contamination.
  • The proper choice of aluminum filler metal mainly depends on the base metal properties to be achieved andwelding technique. Post weld cracking, corrosion resistance and behavior under elevated temperature also needto be taken into consideration.
  • Cracking usually can be minimized by choosing a filler metal alloy of higher alloy content then the base metal.

 

Composition:

  • Deposited Chemical Composition % (Typical)
  • Deposited chemistry is influenced by many factors so no typical analysis can be reported.